Automotive Radiator Scrap
Shredded copper-brass radiator cores from vehicles containing 65-75% copper, zinc dominant per subheading note (a). Classified as low-copper content scrap under 7404.00.30. Common recycling stream from end-of-life autos.
Import Duty Rates by Country of Origin
More Specific Codes
This product may fall under a more specific subheading:
Alternative Classifications
This product could be classified differently depending on its characteristics or intended use.
If imported as complete used radiators, not dismantled scrap
Complete auto parts classified by function in Chapter 87, not as waste/scrap.
If high copper turnings/borings from radiator manufacturing
Machining waste >94% Cu classified separately from fabricated scrap.
If contaminated with >50% ferrous iron content
Ferrous scrap dominates classification per material weight predominance.
Not sure which classification is right?
Our AI classifier can analyze your specific product and recommend the correct HTS code with confidence.
Import Tips & Compliance
• Submit detailed chemical analysis showing brass composition; customs may test samples
• Remove steel attachments completely to prevent reclassification as mixed metal scrap
• Comply with TSCA import requirements for processed scrap materials
Related Products under HTS 7404.00.30
Brass Plumbing Scrap
Waste brass fittings, valves, and pipes from plumbing fixtures with copper content typically 60-70% by weight, mixed with zinc predominant. Classified under HTS 7404.00.30 as copper-zinc base alloy scrap below 94% copper threshold per subheading note (a). Excludes high-purity copper scrap.
Yellow Brass Turnings
Machining turnings from yellow brass (Cu 65%, Zn 35%) with copper below 94% threshold. Subheading note (a) defines as copper-zinc base alloy scrap. Generated from lathe operations on brass components.
Bronze Bearing Scrap
Scrap from phosphor bronze bushings/bearings (Cu 88%, Sn 10%, P trace) with copper <94%. Meets subheading note (b) copper-tin base alloy definition. From industrial machinery rebuilds.
Brass Shell Casings Scrap
De-milled military/police brass cartridge cases (70% Cu, 30% Zn) with copper <94%. Classic brass scrap per subheading note (a). Requires demilitarization certification.
Naval Brass Propeller Scrap
Corroded naval brass (63% Cu, 36% Zn, 1% Sn) propeller fragments from marine salvage, copper <94%. Copper-zinc alloy per note (a). Saltwater exposed scrap.
Red Brass Pipe Scrap
Scrap red brass (85% Cu, 15% Zn) water meter bodies and pipes, still <94% copper. Borderline copper-zinc alloy per note (a). From plumbing replacement projects.